Cawiton® MT910
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Wittenburg B.V. |
| Trademark: | Cawiton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O2GGIz_Cawiton-MT910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cawiton MT910 is a Styrene Ethylene Butylene Styrene Block Copolymer (SEBS) material. It is available in Europe for injection molding. Important attributes of Cawiton MT910 are:
Typical application of Cawiton MT910: Medical/Healthcare |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 10 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 0.400 | MPa | |
| Flow : 100% Strain | 0.700 | MPa | |
| Across Flow : 200% Strain | 0.500 | MPa | |
| Flow : 200% Strain | 0.800 | MPa | |
| Across Flow : 300% Strain | 0.700 | MPa | |
| Flow : 300% Strain | 0.900 | MPa | |
| Tensile Stress | ISO 37 | ||
| Across Flow : Yield | 1.50 | MPa | |
| Flow : Yield | 0.800 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 630 | % | |
| Flow : Break | 370 | % | |
| Tear Strength | ISO 34-1 | ||
| Across Flow | 12 | kN/m | |
| Flow | 7.4 | kN/m | |
| Compression Set (70°C, 22 hr) | 48 | % | ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) 1 | 166 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 30.0 to 60.0 | °C | |
| Rear Temperature | 160 to 200 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 180 to 220 | °C | |
| Processing (Melt) Temp | 160 to 220 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Measured with a differential scanning calorimeter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ SX 218 V60 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL STAR™ |
| Abstron IM11BM | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Hostacom 68F4-3 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| MAJORIS DEG368X - 8432 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 2960-80 White 1500 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |