MarFlex® 9608XD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O25gg7_MarFlex-9608XD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex® 9608XD is a High Density Polyethylene material. It is available in Latin America or North America for cast film or coextrusion. Important attributes of MarFlex® 9608XD are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.962 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Cast Film | 758 | MPa | |
| 1% Secant, TD : 32 µm, Cast Film | 841 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 32 µm, Cast Film | 29.0 | MPa | |
| TD : Break, 32 µm, Cast Film | 23.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Cast Film | 870 | % | |
| TD : Break, 32 µm, Cast Film | 790 | % | |
| Water Vapor Transmission Rate (32 µm, Cast Film) | 5.0 | g/m²/24 hr | ASTM F1249 |
| Dart Drop Test - Cast Film (31.8 µm) | 13.5 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 13.5 | kN/m | |
| TD : 31.8 µm | 38.6 | kN/m |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 31.8 µm, Cast Film) | 120 | ASTM D2457 | |
| Haze (31.8 µm, Cast Film) | 11 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 7400H | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| 4LAC® 25H20000 | 4Plas | ABS | 4LAC® |
| Leona™ 13G50 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| LNP™ THERMOCOMP™ DC0049XF compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Sylvin 7843-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |