VALOX™ DR48 - CS1049 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O1i12L_VALOX-DR48---CS1049-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX DR48 is a 15 % glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromotor housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.50 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 8.00 | cm³/10min | |
| 250°C/5.0 kg | 24.0 | cm³/10min | |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 0.50 to 0.80 | % | |
| Across Flow | 0.60 to 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.17 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 102 | MPa | |
| Break | 102 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.0 | % | |
| Break | 3.0 | % | |
| Flexural Modulus 2 | 5200 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 16.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 3 | 4.0 | kJ/m² | ISO 179/1eA |
| -30°C | 5.0 | kJ/m² | ISO 179/2C |
| 23°C 4 | 5.0 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 0°C | 5.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | 27 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7(1.8 MPa, Unannealed, 64.0 mm Span) | 170 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 200 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | |
| Flow : 23 to 80°C | 3.5E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 2.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 9.5E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.19 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | |||
| 0.800 mm, in Oil | 29 | kV/mm | ASTM D149, IEC 60243-1 |
| 1.60 mm, in Oil | 23 | kV/mm | ASTM D149, IEC 60243-1 |
| 3.20 mm, in Oil | 16 | kV/mm | ASTM D149, IEC 60243-1 |
| 1.00 mm 8 | 19 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.10 | ASTM D150, IEC 60250 | |
| 50 Hz | 3.20 | IEC 60250 | |
| 60 Hz | 3.20 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.012 | ASTM D150, IEC 60250 | |
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| Arc Resistance 9 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | |
| Solution B | 150 | V | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.890 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 31 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 15 | % | ASTM D229 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| 8 . | Short-Time |
| 9 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ F107BV | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Queo™ 0219 | Borealis AG | Plastomer | Queo™ |
| MTEGRITY™ PS General Purpose GS218 | M. Holland Company | PS (GPPS) | MTEGRITY™ PS General Purpose |
| Karina NATURAL PVC COMPOUND -E 730D25/ 1-IS-WK | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 699 X 121289 A | RTP Company | ABS | RTP |