HOPELEX AN-3800
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | HOPELEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O1WUtK_HOPELEX-AN-3800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS with balanced flowability, impact properties and hydrolytic stability Non-brominated, non-chlorinated flame retardant Heat resistance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 80 | % | ASTM D638 |
| Flexural Modulus 3 | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | V-0 5VB | ||
| 3.00 mm | V-0 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanoblend™ MB 1201 | PolyOne Corporation | PP Impact Copolymer | Nanoblend™ |
| Next Nylon 6 Prime Series NGF20-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| ACRYLITE® Sheet Resist 45 | Evonik Cyro LLC | Acrylic, Unspecified | ACRYLITE® Sheet |
| Baoding 67I70 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Hiprolon® 70 MNWHL G30 | Arkema | Nylon 610 | Hiprolon® |