TAROMID A 280 Z3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O1I8PU_TAROMID-A-280-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 elastomer modified, very high impact resistance, good impact also at low temperature, good chemical resistance to oils, solvents and other chemical substances. Available: different colors, UV-stabilized (L), release agent (W). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.5 to 1.7 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 1.2 | % | ASTM D570, ISO 62 |
| Saturation | 6.0 | % | ASTM D570 |
| Saturation, 23°C | 6.0 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 75.0 | MPa | ISO 178 |
| Break | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| 23°C 2 | 55 | kJ/m² | ASTM D256 |
| 23°C | 55 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -25°C, 3.20 mm | 640 | J/m | ISO 180, ASTM D256 |
| 23°C, 3.20 mm | 700 | J/m | ISO 180, ASTM D256 |
| 23°C 3 | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 66.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50, ASTM D1525 4 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | Type 1, Edgewise, Notch A |
| 3 . | 4 mm |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solef® 1015 | Solvay Specialty Polymers | PVDF | Solef® |
| Forprene® 665M99A60 | SO.F.TER. SPA | TPV | Forprene® |
| EMPILON® 530 | EMPILON | SEBS | EMPILON® |
| LNP™ LUBRICOMP™ KL004U compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| neogol® A90 2 Z005 | API SpA | TPO (POE) | neogol® |