Larton K/30
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O0UBZq_Larton-K-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyphenylene Sulphide (PPS). UL94 V-0 classified, halogens free. Carbon fibre. Very good chemical resistance. Very good thermal resistance. Low smoke toxicity index and optical density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.15 to 0.25 | % | |
| Flow : 2.00 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 25000 | MPa | |
| 60°C | 23500 | MPa | |
| 90°C | 21000 | MPa | |
| 120°C | 15000 | MPa | |
| 150°C | 11000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 185 | MPa | |
| Break, 60°C | 165 | MPa | |
| Break, 90°C | 130 | MPa | |
| Break, 120°C | 85.0 | MPa | |
| Break, 150°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.80 | % | |
| Break, 60°C | 0.90 | % | |
| Break, 90°C | 1.3 | % | |
| Break, 120°C | 1.6 | % | |
| Break, 150°C | 1.8 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 270 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 225 | °C | |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 2.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | 6.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® PA11 P40 BLACK | Arkema | Nylon 11 | Rilsan® |
| SUSTAMID 6G M OL | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| TOPAS® 6013S-04 | Polyplastics Co., Ltd. | COC | TOPAS® |
| GAPEX® HP RPP30EB88HB | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| SABIC® EPDM 657 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |