CYCOLOY™ MC1300 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O0OFDi_CYCOLOY-MC1300-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY MC1300 resin is an injection moldable PC/ABS blend with excellent flow and impact performance. It is designed for plating applications mostly used in the automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 50.3 | MPa | |
| Break | 44.1 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 8.6 | % | |
| Break | 150 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2070 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 430 | J/m | |
| 23°C | 530 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 33.9 | J | |
| 23°C, Total Energy | 40.7 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 116 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 98.9 | °C | |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 to 104 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 249 to 282 | °C | |
| Middle Temperature | 254 to 288 | °C | |
| Front Temperature | 254 to 288 | °C | |
| Nozzle Temperature | 260 to 288 | °C | |
| Processing (Melt) Temp | 260 to 288 | °C | |
| Mold Temperature | 76.7 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Velocity® LCF50-PA66 | PlastiComp, Inc. | Nylon 66 | Velocity® |
| DJSilicone NE-130 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Gallonprene® GP210-7002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Huafon JF-P-6760 / JF-I-6722 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| MAJORIS DG324X - 8229 | AD majoris | PP, Unspecified | MAJORIS |