Fibrolon® P 7550
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Fibrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | O0MsAO_Fibrolon-P-7550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Natural fibre reinforced compound for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Apparent Density | 0.46 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 13 - 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 - 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | ISO 527-2 |
| Fracture | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 3550 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 32.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 4.0 | % | ISO 178 |
| Tensile Strain at Tensile Strength | 3.0 | % | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.9 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 139 | °C | ISO 306/A |
| Melting Temperature (DSC) | 150 - 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Rear Temperature | 150 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 190 | °C | |
| Nozzle Temperature | 200 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 200 | MPa | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding Pressure Level: 50 to 80%Melt Cushion (of volume): <10%Cooling Time: 10 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SFX-19250BM | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| STERalloy™ FDG 2380 | Hapco Inc. | TP, Unspecified | STERalloy™ FDG |
| DOWLEX™ 2078G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Karina RED COLOR CONCENTRATE -E 42/268-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYCOMPO PE 2540R | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |