| E 8353-706R-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.98 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.25 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 78.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 18000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 120 | MPa | ASTM D790 |
| Compressive Strength | 250 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | > 282 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE | ASTM E831 | ||
| Flow | 2.2E-5 | cm/cm/°C | |
| Transverse | 2.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | |||
| -- | 18 | kV/mm | ASTM D149 |
| -- | 14 | kV/mm | ASTM D149 |
| -- | 15 | kV/mm | ASTM D149 |
| Dielectric Constant 1(1 MHz) | 4.40 | ASTM D2520 | |
| Dissipation Factor 2(1 MHz) | 0.019 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet |
| 2 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| En Chuan 6120TA | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Osterlene® PPH-3.5-LWC | Osterman & Company | PP Homopolymer | Osterlene® |
| Petro Rabigh PE F0554 | Rabigh Refining & Petrochemical Co. | HDPE | Petro Rabigh PE |
| TechnoElast S A6002 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |
| EnviroASA 1125 | West Michigan Compounding | ASA | EnviroASA |