Sarlink® TPE RV-2235B-01 XRD (PRELIMINARY DATA) Datasheet,TPE,Teknor Apex Company-SHANGHAI SUSHENG

Message
Sarlink RV-2235B-01 XRD is a high performance thermoplastic elastomer used in a variety of transportation applications including exterior automotive and RV parts. Sarlink RV-2235B-01 XRD is a medium hardness, low density extrusion grade that exhibits sunlight resistance.

General Information
Features	Low Specific Gravity Sunlight Resistant Low density smoothness Light stabilization Medium liquidity Lubrication Fill Hardness, low UV absorption
Uses	Application in Automobile Field Automotive exterior parts Car exterior decoration
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.950	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	10	g/10 min	ASTM D1238

Hardness	Nominal Value	Test Method
Durometer Hardness		ISO 868
Shore A, 1 second, injection molding	44	ISO 868
Shore A, 5 seconds, injection molding	42	ISO 868
Shore A, 15 seconds, injection molding	41	ISO 868

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ISO 37
Transverse flow : 100% strain	0.730	MPa	ISO 37
Flow : 100% strain	1.90	MPa	ISO 37
Tensile Stress ²			ISO 37
Transverse flow : Fracture	6.20	MPa	ISO 37
Flow : Fracture	2.40	MPa	ISO 37
Tensile Elongation ³			ISO 37
Transverse flow : Fracture	870	%	ISO 37
Flow : Fracture	240	%	ISO 37
Tear Strength ⁴			ISO 34-1
Transverse flow	12	kN/m	ISO 34-1
Flow	23	kN/m	ISO 34-1
Compression Set ⁵			ISO 815
23°C, 22 hr	11	%	ISO 815
70°C, 22 hr	60	%	ISO 815
90°C, 70 hr	71	%	ISO 815
125°C, 70 hr	84	%	ISO 815

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air ⁶			ISO 188
Transverse flow : 110°C, 1008 hr	40	%	ISO 188
Flow : 110°C, 1008 hr	0.0	%	ISO 188
Transverse flow : 100% strain 110°C, 1008 hr	11	%	ISO 188
Flow : 100% strain 110°C, 1008 hr	9.5	%	ISO 188
Transverse flow : 125°C, 168 hr	-42	%	ISO 188
Flow : 125°C, 168 hr	-4.2	%	ISO 188
Transverse flow : 100% strain 125°C, 168 hr	-2.7	%	ISO 188
Flow : 100% strain 125°C, 168 hr	5.3	%	ISO 188
Change in Tensile Strain at Break in Air ⁷			ISO 188
Transverse flow : 110°C, 1008 hr	9.4	%	ISO 188
Flow : 110°C, 1008 hr	42	%	ISO 188
Transverse flow : 125°C, 168 hr	95	%	ISO 188
Flow : 125°C, 168 hr	41	%	ISO 188
Change in Shore Hardness in Air
Shao A, 110°C, 1008 hr ⁸	3.1		ISO 188
Shao A, 110°C, 1008 hr ⁹	3.5		ISO 188
Shao A, 125°C, 168 hr ¹⁰	2.2		ISO 188
Shao A, 125°C, 168 hr ¹¹	2.3		ISO 188
Shao A, 125°C, 168 hr ¹²	2.1		ISO 188

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	209	Pa·s	ASTM D3835

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	182 - 232	°C
Cylinder Zone 2 Temp.	188 - 238	°C
Cylinder Zone 3 Temp.	193 - 243	°C
Cylinder Zone 5 Temp.	199 - 249	°C
Die Temperature	199 - 249	°C

Extrusion instructions
Screw Speed: 30 to 100 rpm;Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C).

Note Message
1 .	Type 1, 510mm/min
2 .	Type 1, 510mm/min
3 .	Type 1, 510mm/min
4 .	B method, right angle specimen (without cut), 510mm/min
5 .	Type a
6 .	Type 1
7 .	Type 1
8 .	1 sec
9 .	15 sec
10 .	5 sec
11 .	15 sec
12 .	1 sec

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Sarlink® TPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	NzlqyF_SarlinkTPERV2235B01XRDPRELIMINARYDATA.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2000 B-430	RTP Company	PSU Alloy	RTP
POLYLAN AG15A0	POLYMA Kunststoff GmbH & Co. KG	ABS	POLYLAN
Star L POM D36	Eurostar Engineering Plastics	Acetal (POM) Copolymer	Star L
SUMIKASUPER® LCP E6010	Sumitomo Chemical Co., Ltd.	LCP	SUMIKASUPER® LCP
Kepital® F20-52G	KEP Americas	Acetal (POM) Copolymer	Kepital®