Menzolit® SMC 0200
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NzGHpz_Menzolit-SMC-0200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0200 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 0200 is a general purpose SMC for a wide range of applications. Typically, it is used as housings, covers and functional components in mechanical engineering. The flammability meets the demands of standard UL 94 category HB, on request category V0 is available. The glass content is on a level that combines good mouldability with good mechanical properties regarding strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.15 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 60.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 9000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 142 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 64 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 95 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P601 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| MTEGRITY™ PP Impact Copolymer CP100 | M. Holland Company | PP Impact Copolymer | MTEGRITY™ PP Impact Copolymer |
| HAIPLEN H30 K6 BA X0 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Hifax BA65H | LyondellBasell Industries | PP Copolymer | Hifax |
| Petrotene® PP A3 G50 HS PRTA010 PH384 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |