Ultramid® 8333G HI HS BK-106
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nz94Zk_Ultramid-8333G-HI-HS-BK-106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8333G HI HS BK-106 is a 33% glass reinforced, impact modified PA6 injection molding compound pigmented black developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness and excellent moldability/surface aesthetics. Applications Ultramid 8333G HI HS BK-106 is generally recommended for application such as front wheel chair wheels, bicycle wheels, power tool housings, chain saw housings, clips and fasteners, hose clamps and window hardware. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | |||
| 24 hr | 0.90 | % | ASTM D570 |
| 23°C, 24 hr | 0.90 | % | ISO 62 |
| Saturation | 5.5 | % | ASTM D570 |
| Saturation, 23°C | 5.5 | % | ISO 62 |
| Equilibrium, 50% RH | 1.5 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 145 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 7990 | MPa | ASTM D790 |
| 23°C | 7910 | MPa | ISO 178 |
| Flexural Strength (23°C) | 232 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 208 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 245 to 275 | °C | |
| Middle Temperature | 260 to 285 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1499 X 130922 A | RTP Company | PESU | RTP |
| Staramide AG7 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| EPIMIX POM IMP NC B001 | EPSAN Plastik SAN. ve TiC. A.S. | Acetal (POM) Copolymer | EPIMIX |
| Keysor PVC B450 | Keysor-Century Corporation | PVC, Unspecified | Keysor PVC |
| Diamond GP-525 X | Pak Petrochemical Industries (Pvt.) Ltd. | PS (GPPS) | Diamond |