Hytrel® HTR8341C BK320
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NyiAGo_Hytrel-HTR8341C-BK320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 Shore D, Lubricated, High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.50 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 40 | ||
| Shore D, 15 sec | 37 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 80.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 28.0 | MPa | |
| 10% Strain | 7.00 | MPa | |
| 50% Strain | 12.0 | MPa | |
| 100% Strain | 13.0 | MPa | |
| 300% Strain | 23.0 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 350 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 120 | kN/m | |
| Flow | 110 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Partial Break | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 56.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 42.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -100 | °C | ISO 974 |
| Glass Transition Temperature 1 | -40.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 207 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Transverse | 2.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 8.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.030 | ||
| 1 MHz | 9.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPSiV™ 4200-80A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| WELLAMID Nylon 6000 GV 25 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ALTECH® PE HD A 2010/506 GF10 | ALBIS PLASTIC GmbH | HDPE | ALTECH® PE |
| Formolene® E922 | Formosa Plastics Corporation, U.S.A. | HDPE, MMW | Formolene® |
| Edgetek™ PA-60GF/000 BK006 | PolyOne Corporation | HPPA | Edgetek™ |