| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Dry Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nyi8uf_GeonVinylDryBlendEP680.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™Vinyl Dry Blend EP680 is a rigid PVC product,. It can be processed by extrusion and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-23334-32-0000 | ASTM D4216 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shao D, 6.15mm | 80 | ASTM D2240 | |
| Shao D, 15 seconds, 6.15mm | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(25°C, 3.05 mm) | 3170 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 25°C, 3.05mm) | 41.9 | MPa | ASTM D638 |
| Flexural Modulus 3(25°C, 2.97 mm) | 3650 | MPa | ASTM D790 |
| Flexural Strength 4(25°C, 2.97 mm) | 85.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact - Across Flow (23°C, 3.02mm, molded) | 100 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 5 | 89.8 | J/cm | ASTM D4226 |
| 23°C 6 | > 117 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, unannealed, 12.8mm, compression molding | 74.9 | °C | ASTM D648A |
| 0.45 MPa, annealing, 12.8mm 7 | 74.4 | °C | ASTM D648A |
| 1.8 MPa, unannealed, 12.7mm, molded | 68.7 | °C | ASTM D648A |
| 1.8 MPa, annealed, 12.7mm, molded 8 | 73.2 | °C | ASTM D648A |
| CLTE - Flow (-30 to 30°C, mm) | 5.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 5VA | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | 13 mm/min |
| 4 . | 13 mm/min |
| 5 . | Program A, C.125 Dart |
| 6 . | Program B, C.125 Dart |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-1220HF | QTR, Inc. | PC Alloy | QR Resin |
| DOW™ MDPE DMDA-8962 NT 7 | The Dow Chemical Company | MDPE | DOW™ MDPE |
| Ebalta MG 707 / Z 400 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| PLUSTEK PB320G6 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Rotuba CAB B900 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |