ElectriPlast® EP-CF/PC
| Category: | PC , Polycarbonate |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NyaXXX_ElectriPlast-EP-CF-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-CF/PC is a polycarbonate (PC) product that contains nickel-plated carbon fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7730 | MPa | ASTM D638 |
| Tensile Strength (Break) | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 6730 | MPa | ASTM D790 |
| Flexural Strength | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 57 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | 43 | ohms·cm | ASTM D257 |
| Static Decay | msec | Internal method | |
| Surface Resistance | 18 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| No Burn | HB | UL 94 | |
| t1 or t2 <10 sec. | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 | °C | |
| Middle Temperature | 293 | °C | |
| Front Temperature | 293 | °C | |
| Nozzle Temperature | 288 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 2.07 | MPa | |
| Screw Speed | 82 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 1000 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 DEL | RTP Company | Acetal (POM) Homopolymer | RTP |
| SUPRAN® LFT PP 1340E | SAMBARK | PP, Unspecified | SUPRAN® LFT PP |
| TYNEA 3500 | Tyne Plastics LLC. | Acetal (POM) Homopolymer | TYNEA |
| FHR EPS 54-7654 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Plasmer 7070N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |