NORYL™ FXN119BK resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NyNWEy_NORYL-FXN119BK-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL FXN119BK is a low gloss PPE/HIPS grade. It provides a balance of mechanical properties and heat performance with intrinsic low gloss appreance. FXN119BKBK is available in black only. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2/50 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 48.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.1 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/50 |
| Break 5 | 40 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2200 | MPa | ASTM D790 |
| -- 7 | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 77.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 85.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 75.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 160 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 11 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 42.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 133 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 117 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ASTM D1525 14 |
| -- | 139 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°, Untextured) | 20 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 260 to 285 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 265 to 285 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RETARDEL™ LSF-15 | HELLENIC CABLES S.A. | Polyolefin, Unspecified | RETARDEL™ |
| Versaflex™ OM 9-801N | PolyOne Corporation | TPE | Versaflex™ |
| Trademark PP PPC150E | Trademark Plastics Corporation | PP Impact Copolymer | Trademark PP |
| ALCUDIA® EVA PA-465 | REPSOL | EVA | ALCUDIA® EVA |
| Hostalen GM 5010 T3 S blue | LyondellBasell Industries | HDPE | Hostalen |