SCHULADUR® A3 GF 30 K2224
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NvVGzR_SCHULADUR-A3-GF-30-K2224.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Blend PBT/ASA with 30% glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 184 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 118 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 48 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ISO 306/A50 |
| -- | 145 | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | 16 | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 700 | °C | |
| 3.00 mm | 750 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 725 | °C | |
| 3.00 mm | 775 | °C | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO MUH DN1300 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Trithene® SX 9003 | Petroquimica Triunfo | MDPE | Trithene® |
| CYCOM® 2040 | Cytec Industries Inc. | Epoxy | CYCOM® |
| Formolene® 5143C | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Karina GRAY PVC COMPOUND 802-18/462-C-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |