AKROMID® A3 GF 30 S1 black (3723)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nuimwe_AKROMID-A3-GF-30-S1-black-3723-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 S1 black (3723) is a 30% glass fibre reinforced, cold impact strength polyamide 6.6 with high stiffness and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 | % | |
| Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8000 | MPa | ISO 178 |
| Flexural Stress 2 | 255 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 4.2 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 90 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | °C | ISO 75-2/C |
| Melting Temperature 4 | 262 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6G M OL | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| NORYL™ 6390H resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| Fainplast PVC RH 212/W | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| EPO-TEK® 360 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Petlon R-Prime B2-G30-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |