Innothane® IE-80D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NuG2rF_Innothane-IE-80D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-80D is a rigid polyurethane formulated for room temperature hand-batch processing or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. IE-80D is particularly ideal for color-matching applications due to its neutral semi-transparent appearance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.07 | g/cm³ | |
| Cured | 1.12 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2170 | MPa | ASTM D790 |
| Compressive Modulus | 3620 | MPa | ASTM D695 |
| Compressive Strength | 55.2 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 89 | ||
| Demold Time | 240 to 360 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.050 | Pa·s | |
| 25°C 2 | 0.40 | Pa·s | |
| 25°C 3 | 0.80 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 13 to 17 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 69.6 | MPa | ASTM D638 |
| Tensile Elongation at Break | 8.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 575P | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| GLS Nylon 6 PW39 | GLS Polymers Pvt. Ltd. | Nylon 6 | GLS Nylon 6 |
| EL-Lene™ M3804RU | SCG Chemicals Co., Ltd. | LLDPE | EL-Lene™ |
| Panlite® BN-8110R | TEIJIN LIMITED | PC | Panlite® |
| Plaslube® PA6/12 GF33 1001 BK | Techmer Engineered Solutions | Nylon 612 | Plaslube® |