Zytel® 70G35EF NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NuB1dG_Zytel-70G35EF-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced Polyamide 66 Developed for Electrical and Electronics Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % | |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 4.6 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 8400 | MPa | |
| 1000 hr | -- | 6000 | MPa | |
| Flexural Modulus | 10000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | -- | kJ/m² | |
| -30°C | 11 | 10 | kJ/m² | |
| 23°C | 14 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 90 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 13 | -- | kJ/m² | |
| 23°C | 15 | -- | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 6.00 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 110 | -- | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 255 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Transverse | 8.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 31 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.700 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.24 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2130 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.24 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 884 X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| ExxonMobil™ LDPE LD 143.26 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| OmniLon™ PA6/6 U GMR36 HS | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| LEXAN™ XHT3171 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| WELLAMID Nylon 6000 GV 50 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |