Sinkral® B 4 Venezia
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NtRgcB_SinkralB4Venezia.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
B 4 Venezia is an extrusion grade developed for glossy applications.Easily extrudable even in large sheets, it has high gloss and high modulus. Designation: Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 Applications It's used in sectors that need high gloss and good processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 45 | % | ASTM D638 |
| Flexural Modulus 3 | 2150 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | DIN 53453 | |
| 23°C | No Break | DIN 53453 | |
| Notched Izod Impact 5(23°C) | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 109 | °C | ISO 306/A120 |
| -- | 104 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (3.0 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,EGN,105-04-16-20 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC100E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Nipolon® Hard 8022 | TOSOH Corporation | HDPE | Nipolon® Hard |
| Hanwha Total PP GB35F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Keliren® CM366 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| LUVOCOM® 1106-7940/GY | Lehmann & Voss & Co. | PEI | LUVOCOM® |