Ultramid 8202C is a modified crystalline and low viscosity, PA6 injection molding homopolymer. It is also available in heat stabilized (Ultramid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance. Applications Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components.

General Information
Features	Low viscosity Crystallization Homopolymer Workability, good Fast molding cycle Good chemical resistance
Uses	Bushing Gear Electrical/Electronic Applications Electrical components Valve/valve components Furniture Accessories
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Appearance	Available colors
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.13	--	g/cm³	ASTM D792, ISO 1183
Molding Shrinkage - Flow (3.18 mm)	0.90	--	%
Water Absorption
24 hr	1.6	--	%	ASTM D570
23°C, 24 hr	1.6	--	%	ISO 62
Saturation	9.3	--	%	ASTM D570
Saturated, 23°C	9.3	--	%	ISO 62
Balance, 50% RH	2.6	--	%	ASTM D570
Equilibrium, 23°C, 50% RH	2.6	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	120	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus				ISO 527-2
-40°C	4090	--	MPa	ISO 527-2
23°C	3700	1360	MPa	ISO 527-2
80°C	750	--	MPa	ISO 527-2
120°C	550	--	MPa	ISO 527-2
150°C	445	--	MPa	ISO 527-2
Tensile Strength
Yield, -40°C	137	142	MPa	ASTM D638, ISO 527-2
Yield, 23°C	90.0	48.0	MPa	ASTM D638
Yield, 80°C	40.0	30.0	MPa	ASTM D638, ISO 527-2
Yield, 121°C	30.0	25.0	MPa	ASTM D638
Yield, 23°C	88.0	43.0	MPa	ISO 527-2
Yield, 120°C	30.0	25.0	MPa	ISO 527-2
Yield, 150°C	25.0	--	MPa	ISO 527-2
Fracture, -40°C	130	80.0	MPa	ASTM D638
Fracture, 23°C	90.0	70.0	MPa	ASTM D638
Fracture, 80°C	35.0	30.0	MPa	ASTM D638
Fracture, 121°C	25.0	20.0	MPa	ASTM D638
Tensile Elongation
Yield, -40°C	3.0	3.0	%	ASTM D638
Yield, 23°C	4.0	22	%	ASTM D638, ISO 527-2
Yield, 80°C	25	25	%	ASTM D638
Yield, 121°C	27	30	%	ASTM D638
Fracture, -40°C	5.0	3.0	%	ASTM D638
Fracture, 23°C	12	> 100	%	ASTM D638
Fracture, 80°C	> 100	> 100	%	ASTM D638
Fracture, 121°C	> 100	> 100	%	ASTM D638
Nominal Tensile Strain at Break				ISO 527-2
-40°C	5.0	3.0	%	ISO 527-2
23°C	7.0	> 50	%	ISO 527-2
80°C	> 100	> 100	%	ISO 527-2
120°C	> 100	> 100	%	ISO 527-2
Flexural Modulus
-40°C	3370	4200	MPa	ASTM D790
23°C	3170	970	MPa	ASTM D790
65°C	600	--	MPa	ASTM D790
90°C	440	--	MPa	ASTM D790
121°C	385	--	MPa	ASTM D790
23°C	2800	--	MPa	ISO 178
Flexural Strength
-40°C	183	168	MPa	ASTM D790
23°C	110	42.0	MPa	ASTM D790
65°C	30.0	--	MPa	ASTM D790
121°C	21.0	--	MPa	ASTM D790
23°C	95.0	--	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	--	kJ/m²	ISO 179
Charpy Unnotched Impact Strength (23°C)	No Break	--		ISO 179
Notched Izod Impact				ASTM D256
-40°C	32	21	J/m	ASTM D256
23°C	48	170	J/m	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed	190	--	°C	ASTM D648
0.45 MPa, not annealed	165	--	°C	ISO 75-2/B
1.8 MPa, not annealed	75.0	--	°C	ASTM D648
1.8 MPa, not annealed	65.0	--	°C	ISO 75-2/A
Peak Melting Temperature	220	--	°C	ASTM D3418, ISO 3146
CLTE - Flow	8.1E-5	--	cm/cm/°C	ASTM E831
RTI Elec				UL 746
0.71 mm	125	--	°C	UL 746
1.5 mm	125	--	°C	UL 746
3.0 mm	125	--	°C	UL 746
6.0 mm	125	--	°C	UL 746
RTI Imp				UL 746
0.71 mm	65.0	--	°C	UL 746
1.5 mm	75.0	--	°C	UL 746
3.0 mm	75.0	--	°C	UL 746
6.0 mm	75.0	--	°C	UL 746
RTI				UL 746
0.71 mm	65.0	--	°C	UL 746
1.5 mm	85.0	--	°C	UL 746
3.0 mm	85.0	--	°C	UL 746
6.0 mm	85.0	--	°C	UL 746

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity
1.50 mm	> 1.0E+13	--	ohms·cm	ASTM D257
--	> 1.0E+13	--	ohms·cm	IEC 60093
Dielectric Strength ¹(1.50 mm)	30	--	kV/mm	ASTM D149
Comparative Tracking Index	600	--	V	IEC 60112

Flammability	Dry	Conditioned	Test Method
Flame Rating			UL 94
0.71 mm	V-2	--	UL 94
1.5 mm	V-2	--	UL 94
3.0 mm	V-2	--	UL 94
6.0 mm	V-2	--	UL 94

Additional Information	Dry	Conditioned	Unit	Test Method
Drop Weight Impact Strength (23°C)	122	> 271	J	Internal method

Note Message
1 .	Method A (short time)

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Corporation
Trademark:	Ultramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Nt2SQY_Ultramid8202C.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Polylite® ProCast PLUS 32144-40	Reichhold Chemicals, Inc.	Polyester, TS	Polylite® ProCast PLUS
ProvaMed® PVC 5377	ACTEGA GmbH	PVC, Unspecified	ProvaMed® PVC
Vi-Chem PVC VDM87-30E	Vi-Chem Corporation	PVC, Unspecified	Vi-Chem PVC
Sylvin 5132-86 Clear Black 283	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Staramide 6 1565VE10	Eurostar Engineering Plastics	Nylon 6	Staramide