Baytec® OCS 080D
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NslaaS_Baytec-OCS-080D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec OCS 080D is a two-component polyurethane/-urea system that yields an optically clear solid elastomer. The isocyanate component A is an aliphatic isocyanate-terminated (rMDI) polyester prepolymer, and the polyol component is a proprietary polyester formulation. The Baytec OCS 080D system can be used to produce highly transparent, optical/ballistic-grade parts for applications ranging from ophthalmic lenses to bulletproof enclosures. As with any product, the Baytec OCS 080D system must be tested (including field testing, etc) in advance by the user to determine suitability for a given application. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 59.5 | MPa | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 68.1 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.530 | ASTM D542 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | < 0.50 | % | ASTM D1003 |
| Abbe Number | 43.0 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components 1 | |||
| Component a | Mixing ratio by weight: 170 | ||
| Component B | Mixing ratio by weight: 100 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Colorless to pale yellow liquid Specific Gravity @ 25°C: 1.086 Viscosity @25°C: 1378 mPa Flash Point, PMCC: >93°C NCO: 19.6 to 20.3 wt% Bulk Density at 25°C: 9.05 lb/gal Part B Type: Polyol Appearance: Yellow liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 680 mPa-s Flash Point, PMCC: >93°C Bulk Density at 25°C: 8.62 lb/gal Isocyanate Temperature: 25 to 50°CPolyolTemperature: 25 to 50°CMold Temperature: 110°CGel Time: 1:45 minPostcure Temperature: 110°CDemold Time: 2 to 4 minPostcure Time: 16 hr |
| Note Message | |
|---|---|
| 1 . | 105 Index |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COPEC® CC6OCZ (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |
| IDI BMC B30 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI BMC |
| Plaslube® PPA CF30 TL10 | Techmer Engineered Solutions | PPA | Plaslube® |
| POLYCOMPO PE 102 | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |
| LNP™ FARADEX™ AS003 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |