Razalen® P311
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razalen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NsiW6l_Razalen-P311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razalen P311 is a general purpose extrusion grade natural color impact copolymer polypropylene. It combines good toughness as well as excellent processability, chemical, and fatigue resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Flexural Strength | 39.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 60 | J/m | |
| 23°C | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 80.0 | °C | |
| 1.8 MPa, Unannealed | 51.0 | °C | |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3783 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| THERMOLAST® K TF7CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultraform® N 2640 Z6 UNC | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Biomer® P226 | Biomer | Biodeg Polymers | Biomer® |
| Hostaform® XGC25-LW01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |