VALOX™ K3501 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NsbyXx_VALOX-K3501-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive underhood applications requiring USCAR-2 Class III humidity/heat performance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 1.7 to 2.6 | % | |
| Across Flow : 3.20 mm | 1.7 to 2.6 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.34 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2430 | MPa | ASTM D638 |
| -- | 2030 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 49.4 54.0 | MPa | ASTM D638 |
| Yield | 50.7 | MPa | ISO 527-2/50 |
| Break 3 | 37.0 24.3 | MPa | ASTM D638 |
| Break | 73.4 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.0 3.5 | % | ASTM D638 |
| Yield | 3.2 | % | ISO 527-2/50 |
| Break 5 | 25 12 51 | % | ASTM D638 |
| Break | 37 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2330 2360 2080 | MPa | ASTM D790 |
| -- 7 | 2030 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 73.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -20°C | 73 | J/m | ASTM D256 |
| 0°C | 83 | J/m | ASTM D256 |
| 23°C | 89 | J/m | ASTM D256 |
| 23°C 10 | 8.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (-30°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Total Energy | 60.0 | J | |
| 23°C, Total Energy | 61.0 58.0 48.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 46.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 46.4 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 170 | °C | ISO 306/B50, ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 76.7 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2597 | Teknor Apex Company | TPE | Telcar® |
| Sylvin 2814-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CP PRYME® Nylon 6 N140GBHSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| EL-Lene™ H5604F | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Sylvin 4260-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |