Lanufene LLF 183N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Ras Lanuf Oil & Gas Processing Company (RASCO) |
| Trademark: | Lanufene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NsStGq_Lanufene-LLF-183N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LANUFENE LLF 183N is a linear low density polyethylene for cast film extrusion with high mechanical properties and good process-ability. LANUFENE LLF 183N contains neither slip additive nor anti-blocking agent. The film produced from this resin characteristically exhibits good toughness, and outstanding puncture resistance. LANUFENE LLF 183N is particularly suitable for the manufacture of PE Cast Films and other applications where excellent flow properties and good mechanical properties are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 15.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm | 150 | MPa | |
| 1% Secant, TD : 38 µm | 154 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm | 30.0 | MPa | |
| TD : Break, 38 µm | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 450 | % | |
| TD : Break, 38 µm | 650 | % | |
| Dart Drop Impact (38 µm) | 120 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 90 | ASTM D2457 | |
| Haze (38.0 µm) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B4660AB | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Nypol® PA B3 G30 HS PRTA011 NT351 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| BMC T60-6009 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| ENFLEX S4055A CL NAT | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Sylvin 9604-90 Blue 8432 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |