DynaMix Lite™ 3144-GHIL
| Category: | PEI , Polyether Imide |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaMix Lite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NsBqIX_DynaMix-Lite-3144-GHIL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass Filled Impact Modified PEI Features:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 to 8.0 | % | ASTM D638 |
| Flexural Modulus | 4690 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 332 to 374 | °C | |
| Middle Temperature | 338 to 377 | °C | |
| Front Temperature | 343 to 382 | °C | |
| Nozzle Temperature | 343 to 388 | °C | |
| Processing (Melt) Temp | 343 to 388 | °C | |
| Mold Temperature | 121 to 177 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 20 to 100 | rpm | |
| Clamp Tonnage | 5.5 to 8.3 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Complet® LGF30-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Comco PA 6 G heat stabilized | Comco-Plastic GmbH | Nylon 6 | Comco |
| ColorFast® FRA202 | LTL Color Compounders, Inc. | ABS | ColorFast® |
| LubriOne™ NN-000/15T BLACK | PolyOne Corporation | Nylon 66 | LubriOne™ |
| OxyVinyls® 280 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |