Order Products : sales@su-jiao.com
LEXAN™ HPH4504H resin
| Category: | PPC , Polyphthalate Carbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqgDmi_LEXANHPH4504Hresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High heat specialty polycarbonate with enhanced autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 of USP Class VI). EtO, steam, gamma and e-beam sterilizable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| -- | 1.19 | g/cm³ | ASTM D792 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 3.00 | cm³/10min | ISO 1133 |
| 330°C/2.16 kg | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 - 0.80 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.16 | % | ASTM D570 |
| Saturated, 23°C | 0.16 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 85 | ASTM D785 | |
| Class r | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2090 | MPa | ASTM D638 |
| -- | 2260 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.5 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Fracture 3 | 71.7 | MPa | ASTM D638 |
| Fracture | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture 5 | 120 | % | ASTM D638 |
| Fracture | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2030 | MPa | ASTM D790 |
| -- 7 | 2130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 66.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 95.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 640 | J/m | ASTM D256 |
| -30°C 10 | 11 | kJ/m² | ISO 180/1A |
| 23°C 11 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 73.0 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 149 | J | ASTM D3029 |
| Tensile Impact Strength 12 | 578 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 132 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ASTM D1525 14 |
| -- | 154 | °C | ISO 306/B50 |
| -- | 155 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -40 to 95°C | 9.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 2.6E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.15 | ASTM D150 | |
| 60 Hz | 3.15 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.2E-3 | ASTM D150 | |
| 60 Hz | 1.2E-3 | ASTM D150 | |
| 100 Hz | 0.024 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.600 | ASTM D542 | |
| Transmittance (2540 µm) | 85.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 316 - 338 | °C | |
| Middle Temperature | 327 - 349 | °C | |
| Front Temperature | 338 - 360 | °C | |
| Nozzle Temperature | 332 - 354 | °C | |
| Processing (Melt) Temp | 338 - 360 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | Type S |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1960T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Tenite™ Propionate 360E4861312 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| STARFLEX® P 7002 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | STARFLEX® |
| KOPLA PA66 KDG1040 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| PERCOM® KHT10 | A. Schulman Europe | PP Homopolymer | PERCOM® |