Order Products : sales@su-jiao.com
TPX® DX350
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqSXCB_TPX-DX350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX® DX350 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for extrusion coating or fiber (spinning) extrusion. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.833 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 110 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 29.0 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 14 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 41.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 19 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 124 | °C | ASTM D648 |
| Vicat Softening Temperature | 169 | °C | ASTM D1525 |
| Melting Temperature | 233 | °C | DSC |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 66 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 | ASTM D542 | |
| Transmittance | 93.0 | % | ASTM D1003 |
| Haze | 2.1 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DAULEN PPH GF 30 | Daunia Trading srl | PP Homopolymer | DAULEN |
| Dryflex® A1 602601 | ELASTO | SEBS | Dryflex® |
| Kumho ABS H2938Z | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Karina WHITE PVC COMPOUND 800-10/177-Y-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 916VO-95 Brown 7385 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |