Radilon® A ECP3808 339 NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqOpzQ_Radilon-A-ECP3808-339-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 30% mineral filled injection moulding grade. Toughened. Black colour Suitable for parts requiring improved impact strength along with surface planarity. ISO 1043 : PA66-I-MD30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 5.8 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3050 | 1550 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | |||
| Yield | -- | 35.0 | MPa | |
| Break | 55.0 | -- | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | |||
| Yield | -- | 19 | % | |
| Break | 10 | -- | % | |
| Nominal Tensile Strain at Break | -- | 35 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 2800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | 5.0 | kJ/m² | |
| 23°C | 6.5 | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 65 | kJ/m² | |
| 23°C | 70 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 150 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 10 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6003 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| Vi-Chem PVC VSR87-80E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| Ablebond 77-2LTC | Henkel Ablestik | Epoxy | Ablebond |
| ICORENE® N2808 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| LNP™ LUBRICOMP™ DP0039EF compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |