GELOY™ XP4045LG resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqNsKh_GELOY-XP4045LG-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Available in a wide range of colors. Recommended for weatherable/unpainted interior/low gloss/high heat applications. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.60 to 0.90 | % | |
| Across Flow : 3.20 mm | 0.60 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2330 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.2 | % | |
| Break | 47 | % | |
| Flexural Modulus 1 | 2270 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C 2 | 12 | kJ/m² | |
| -30°C 3 | 14 | kJ/m² | |
| 23°C 4 | 25 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -40°C | 8.0 | kJ/m² | |
| -30°C | 8.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 15.0 | J | |
| -30°C, Total Energy | 17.0 | J | |
| 23°C, Energy at Peak Load | 45.0 | J | |
| 23°C, Total Energy | 53.7 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 125 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 103 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 126 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -30 to 80°C | 6.7E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 250 to 275 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Processing (Melt) Temp | 265 to 285 | °C | |
| Mold Temperature | 50.0 to 82.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV3-2500 | NuSil Technology | Silicone | NuSil |
| Adell Polyamide BD-10 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| KumhoSunny AES HW600FR | Shanghai KumhoSunny Plastics Co., Ltd. | AES | KumhoSunny AES |
| Karina CLEAR PVC COMPOUND 80/221-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-0866/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |