Order Products : sales@su-jiao.com
Alkathene® XJF143
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqGVoG_Alkathene-XJF143.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
XJF143 is a low density polyethylene designed for a variety of low gauge (20 - 50µm) general purpose film applications. XJF143 does not contain any additives. XJF143 is intended for use in a variety of general purpose film applications, typically of the thickness 20 to 50µm, and blending into other film grades |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 32 µm | 150 | MPa | ASTM D882 |
| 2% secant, TD : 32 µm | 180 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 32 µm | 22.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm | 17.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 290 | % | ASTM D882 |
| TD : Broken, 32 µm | 810 | % | ASTM D882 |
| Dart Drop Impact (32 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 420 | g | ASTM D1922 |
| TD : 32 µm | 180 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 32.0 µm, blown film) | 77 | ASTM D2457 | |
| Haze (32.0 µm, blown film) | 5.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1985NT | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Miramid® S3CW | BASF Leuna GmbH | Nylon 66 | Miramid® |
| Fainplast PVC PMP 001/14 | Fainplast Compounds S.r.l | PVC+PUR | Fainplast PVC |
| Hanwha Total PP TB71S | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Sylvin 916VO-95 White 1469 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |