BESTDUR TH/02
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTDUR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NqEFZy_BESTDUR-TH-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT black Standard lubrified to gain improvements in injection and moulding, is a generic use PBT. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 245 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO B1101 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Teslin® SP 1000 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| EUROPLEX® Sheet PPSU 99460 | Evonik Industries AG | PPSU | EUROPLEX® Sheet |
| Lucofin® 1461 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Sylvin 9067-85LMW GREY 9269 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |