LNP™ THERMOCOMP™ RF007SXR compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nq6cM2_LNP-THERMOCOMP-RF007SXR-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF007SXR is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material includes: Heat Stabilized, Hydrolysis Resistant. Also known as: LNP* THERMOCOMP* Compound RF007SXR Product reorder name: RF007SXR |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.78 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 3.0 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.45 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.51 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11900 | MPa | ASTM D638 |
| -- | 11700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 195 | MPa | ASTM D638 |
| Fracture 3 | 175 | MPa | ASTM D638 |
| Fracture | 193 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 2.5 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 5 | 10600 | MPa | ASTM D790 |
| -- 6 | 9840 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 268 | MPa | ISO 178 |
| Yield, 50.0mm span 7 | 285 | MPa | ASTM D790 |
| Fracture, 50.0mm span 8 | 284 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 10 | 61 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.56 | J | ASTM D3763 |
| -- | 3.04 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 261 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 11 | 261 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 255 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 252 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 3.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4702-698UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Synres® SR-4321 | Teknor Apex Company | PP, Unspecified | Synres® |
| ISOTHANE® 5075A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| OTECH PVC OE6037 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Sylvin 9940-60 Orange 591 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |