| FORMULA P COMP 6220 M1 Z is a polypropylene product,. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 21.0 | MPa | ISO 527-2 |
| Fracture | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 56.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -20°C | 2.0 | kJ/m² | ISO 180 |
| 23°C | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 21 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40.0 - 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0437M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| DINAPLEN® PPH1S20 M403 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Elastron® G G400.A52.T | Elastron USA, Inc. | SEBS | Elastron® G |
| Hostaform® C 27021 GV3/30 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Polifil® Nylon 78MRGF | The Plastics Group | Nylon 66 | Polifil® Nylon |