Wellamid® GF33-66 XE-N1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Npdfgs_Wellamid-GF33-66-XE-N1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GF33-66 XE-N1 is a Polyamide 66 (Nylon 66) material filled with 33% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Wellamid® GF33-66 XE-N1: Flame Rated. Typical application of Wellamid® GF33-66 XE-N1: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 8620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 249 | °C | ASTM D648 |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.794 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 76.7 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 282 to 304 | °C | |
| Middle Temperature | 271 to 288 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Nozzle Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 435 | Celanese Corporation | TPC-ET | Riteflex® |
| TECOLITE KM-13B(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Trexprene® D50BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Arnitel® VT3108 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| Cogegum® AFR/765-UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |