Generic PUR-Ether/MDI
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NpLQsi_Generic-PUR-Ether-MDI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PUR-Ether/MDI This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 to 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.59 to 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 39 to 98 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 13.0 to 38.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 to 150 | % | ASTM D638 |
| Flexural Modulus (23°C) | 20.7 to 1230 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 0.0269 to 1.43 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain, 23°C | 2.35 to 19.3 | MPa | |
| 300% Strain, 23°C | 8.43 to 21.2 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Break, 23°C | 15.0 to 24.8 | MPa | |
| 23°C | 15.9 to 51.7 | MPa | |
| Tensile Elongation (Break, 23°C) | 110 to 600 | % | ASTM D412 |
| Tear Strength | |||
| 23°C | 40.7 to 124 | kN/m | ASTM D624 |
| Split | 22 | kN/m | ASTM D470 |
| Compression Set | 4.0 to 51 | % | ASTM D395 |
| Bayshore Resilience | 43 to 65 | % | ASTM D2632 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 260 to 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 1.1E-4 to 1.7E-4 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 1.5 to 8.9 | min | |
| Thermoset Mix Viscosity | 344 to 759 | cP | ASTM D2393 |
| Demold Time | 0.38 to 1400 | min | |
| Post Cure Time | 3.5 to 24 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT20-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| NYLEM® 66 GFR 15 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| Karina WHITE COLOR CONCENTRATE -E 1-/105-FC-LMPA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Infino NH-1029 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |
| Moplen HP522H | LyondellBasell Industries | PP Homopolymer | Moplen |