Ebalta AH 100 / SR
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NohANL_Ebalta-AH-100-SR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 to 88 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3000 to 3600 | MPa | ISO 178 |
| Flexural Stress | 110 to 130 | MPa | ISO 178 |
| Compressive Stress | 90.0 to 110 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 to 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 67.0 to 71.0 | °C | ISO 75-2/B |
| Glass Transition Temperature | 107 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 21 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.08 to 1.18 | g/cm³ | |
| Viscosity (25°C) | 0.85 to 1.1 | Pa·s | |
| Curing Time (20°C) | 5.0 to 7.0 | hr | |
| Pot Life 1(20°C) | 15 to 20 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9710 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Norpex® PPE AX10GF | Custom Resins Group | PPE | Norpex® |
| Hanwha Total PE 8400F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LLDPE | Hanwha Total PE |
| Lumid® GP2251AF | LG Chem Ltd. | Nylon 6 | Lumid® |
| Ultramid® A3HG6 HR | BASF Corporation | Nylon 66 | Ultramid® |