LNP™ LUBRICOMP™ IFL36 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nob4uO_LNP-LUBRICOMP-IFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IFL-4036 Product reorder name: IFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.84 | % | ISO 294-4 |
| Flow : 24 hr | 0.24 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9970 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 154 | MPa | ASTM D638 |
| Break | 157 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.2 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8620 | MPa | ASTM D790 |
| -- | 7920 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 241 | MPa | ASTM D790 |
| -- | 232 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.55 | ||
| vs. Itself - Static | 0.51 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 73 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 17.7 | J | ASTM D3763 |
| -- | 4.27 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 198 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1955 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Zytel® 70G50HSLA BK039B | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Hylon® N2023STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Jampilen HP502R | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Sumikon® PM-6630 (Type: J Black) | SBHPP | Phenolic | Sumikon® |