SCHULABLEND® (ASA/PA) M/MW 6201 MT
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + PA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NoFU90_SCHULABLENDASAPAMMW6201MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nanocomposite based on ASA/PA6 blend with good dimensional stability, high impact strength |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 6.00 | -- | cm³/10min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/10) | 101 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 51.0 | 34.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.1 | 4.7 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 96.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 78.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 184 | -- | °C | ISO 306/A50 |
| -- | 110 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 30 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.5 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.5 mm | 675 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.5 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 700 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y2600T (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Styrolution PS 7800 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| NEFTEKHIM PP 1401D (Q30P) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Ekalon® 26 E I V | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| EPO-TEK® H62 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |