Akulon® K240-HPG3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NnyRLC_Akulon-K240-HPG3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® K240-HPG3 is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for extrusion blow molding. Primary attribute of Akulon® K240-HPG3: Heat Stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.25 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5600 | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 15 | % | ISO 527-2 |
| Flexural Modulus | 5000 | -- | MPa | ISO 178 |
| Flexural Stress | 180 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 20 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 90 | kJ/m² | |
| 23°C | 80 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 255 to 265 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 250 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDM 726 | Marco Polo International, Inc. | LDPE | MARPOL® |
| Royalene® 694 | Lion Copolymer, LLC | EPDM | Royalene® |
| Europrene Latice® 5583 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| DOMAMID® 6G30HCE | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| KumhoSunny ABS HGX4500 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |