LNP™ LUBRICOMP™ DL0039EF compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NnLPUq_LNP-LUBRICOMP-DL0039EF-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DL-0039EF is a compound based on Polycarbonate resin containing 15% PTFE. Characteristics of this grade include: Flame Retardant, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4030 FR Product reorder name: DL0039EF |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.31 | g/cm³ | |
| -- | 1.30 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.60 to 0.80 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2210 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/5 |
| Break 3 | 44.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.4 | % | ASTM D638 |
| Yield | 5.5 | % | ISO 527-2/5 |
| Break 5 | 22 | % | ASTM D638 |
| Break | 27 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2240 | MPa | ASTM D790 |
| -- 7 | 2100 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.35 | ||
| vs. Itself - Static | 0.18 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 6.00 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 140 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 9(23°C) | 1700 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 36.0 | J | ASTM D3763 |
| -- | 35.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 137 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 125 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1400 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Milastomer™ 5030BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| SCHULADUR® PCR GF 15 K1947 | A. Schulman Europe | PBT+PET | SCHULADUR® |
| En Chuan 6133WAL | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Elvaloy® AC 1820 | DuPont Packaging & Industrial Polymers | EMA | Elvaloy® |