VAMPSON L 4010
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NnIff3_VAMPSON-L-4010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Linear PPS, 40% glass fiber reinforced, UL 94 V0 at 1,6 mm, halogen and red phosphorus free, high chemical resistance and excellent operating temperature, good mechanicals properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 160 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648A |
| Vicat Softening Temperature | 255 | °C | ASTM D1525 1 |
| RTI Elec | 200 | °C | UL 746 |
| RTI Imp | 200 | °C | UL 746 |
| RTI Str | 200 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 320 | °C | |
| Mold Temperature | 140 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ NF920 | Asahi Kasei Chemicals Corporation | ACS | Stylac™ |
| TROGAMID® T T5000 | Evonik Industries AG | Nylon 6/3T | TROGAMID® T |
| XANTAR® F 25 UR | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| BESTNYL SI00VI02BX | Triesa Plastics | Nylon 6 | BESTNYL |
| Laprene® 8K1000A70 | SO.F.TER. SPA | SEBS | Laprene® |