LNP™ THERMOCOMP™ SF00A compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NmPMdu_LNPTHERMOCOMPSF00Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass filled Nylon 12 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12800 | MPa | ASTM D638 |
| -- | 12300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 121 | MPa | ASTM D638 |
| Yield | 113 | MPa | ISO 527-2/5 |
| Fracture 3 | 121 | MPa | ASTM D638 |
| Fracture | 113 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.5 | % | ISO 527-2/5 |
| Fracture 5 | 1.8 | % | ASTM D638 |
| Fracture | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 8930 | MPa | ASTM D790 |
| -- 7 | 11.0 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0mm span | 148 | MPa | ASTM D790 |
| Fracture, 50.0mm span | 143 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 97 | J/m | ASTM D256 |
| 23°C 9 | 1.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 10 | 31 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 16.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 176 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 166 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 176 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 232 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 227 - 238 | °C | |
| Mold Temperature | 71.1 - 82.2 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx MPP2A25HC | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| RheTech Polypropylene M15P101-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Dion VER 9100 | Reichhold Chemicals, Inc. | Vinyl Ester | Dion |
| Electrafil® PA6/6 G/CF15 C - 3 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| Hylon® N1033STHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |