Toyolac® TP70 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.06 | g/cm³ | ASTM D792 |
| 23°C | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 29 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 35.0 | MPa | ASTM D638 |
| 23°C | 49.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 10 | % | ASTM D638 |
| Break, 23°C | 10 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2000 | MPa | ASTM D790 |
| 23°C | 1830 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 65.0 | MPa | ASTM D790 |
| 23°C | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 66 | J/m | |
| 23°C, 12.7 mm | 230 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 85.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+9 | ohms | ASTM D257 |
| Electrostatic Voltage 1(23°C) | 290 | V | Internal Method |
| Half-life of Electrostatic Voltage Decay 2(23°C) | 0.3 | sec | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50%, 24 hr |
| 2 . | 50%, 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218G1 V25 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Favorite LL505 | Favorite Plastics | LDPE+LLDPE | Favorite |
| LOXIM 510 01HB | LOXIM Industries Private Limited | PC+ABS | LOXIM |
| Petroquim PP PH 4040 | Petroquim S.A. | PP Homopolymer | Petroquim PP |
| Plaskon CMU-870-2A | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |