Stat-Tech™ PC-15CF/000 FR V0 BK702
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | NloGGZ_Stat-Tech-PC-15CF-000-FR-V0-BK702.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber Reinforced, Non-halogen Containing Flame Retardant Polycarbonate Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 120 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 7500 | MPa | ASTM D790 |
| Flexural Strength 4 | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 - 1.0E+5 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 2208-CR-SX | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Radilon® S 35HR 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| RMA 113/113F | Ronald Mark Associates, Inc. | PVC Copolymer | RMA |
| TARFLON™ NEO AG2240 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |