LNP™ LUBRICOMP™ EX03599H compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nla4bH_LNP-LUBRICOMP-EX03599H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP EX03599H is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-E-03599 EES HC Product reorder name: EX03599H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.28 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.78 | % | ISO 294-4 |
| Flow : 24 hr | 0.72 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3340 | MPa | ASTM D638 |
| -- | 3190 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 105 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2 |
| Break | 88.9 | MPa | ASTM D638 |
| Break | 98.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 7.0 | % | ASTM D638 |
| Yield | 6.8 | % | ISO 527-2 |
| Break | 28 | % | ASTM D638 |
| Break | 9.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3480 | MPa | ASTM D790 |
| -- | 3140 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 152 | MPa | ASTM D790 |
| -- | 112 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.44 | ||
| vs. Itself - Static | 0.45 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 90 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.88 | J | ASTM D3763 |
| -- | 2.56 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 190 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 187 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.1E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3703 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Unichem 8011AG-015 | Colorite Polymers | PVC, Unspecified | Unichem |
| Hylon® N1025THLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Hostacom X 4323 3 S63 100051 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Durethan® B 40 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |