RTP 3405-1

Category: LCP , Liquid Crystal Polymer
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: Nkqoz7_RTP-3405-1.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Glass Fiber
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 30% filler by weight
RoHS Compliance
  • Contact manufacturer
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.62g/cm³ASTM D792
Molding Shrinkage - Flow (3.20 mm)0.10 - 0.20%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Modulus 13800MPaASTM D638
Tensile Strength 165MPaASTM D638
Tensile Elongation (Yield)2.0 - 3.0%ASTM D638
Flexural Modulus 13400MPaASTM D790
Flexural Strength 234MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.20 mm)85J/mASTM D256
Unnotched Izod Impact (3.20 mm)370J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)224°CASTM D648
Additional InformationNominal ValueUnit
Primary Additive 30%
InjectionNominal ValueUnit
Drying Temperature 149°C
Drying Time 4.0hr
Processing (Melt) Temp 271 - 302°C
Mold Temperature 37.8 - 93.3°C
Injection Pressure 34.5 - 82.7MPa
Injection instructions
The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position.
Resin Grade Manufacturer Category Trademark
BMC 3001F Bulk Molding Compounds, Inc. Polyester, TS BMC
Aplax P2515GN Ginar Technology Co., LTD. PP, Unspecified Aplax
Exceed™ 3527PA ExxonMobil Chemical mPE Exceed™
Karina RED MBATCH -E 42/231-GE Karina Ind. e Com. de Plásticos Ltda PVC, Unspecified Karina
ADENE® M38VQEGD00 A.D. Compound S.p.A. PP Copolymer ADENE®