NYLOY® PG-2040N
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Nytex Composites Co., Ltd. |
| Trademark: | NYLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nke4wM_NYLOY-PG-2040N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYLOY® PG-2040N is a Polypropylene material filled with 40% glass fiber. It is available in Asia Pacific or North America for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 | g/cm³ | ASTM D792 |
| -- | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow | 0.48 | % | |
| Across Flow | 1.0 | % | |
| Ash Content | 45 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 106 | ASTM D785 | |
| R-Scale | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 80.4 | MPa | ASTM D638 |
| -- | 81.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7360 | MPa | ASTM D790 |
| -- | 6500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 123 | MPa | ASTM D790 |
| -- | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 160 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 154 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Processing (Melt) Temp | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mar-Bal MB2000-25 | Mar-Bal, Inc. | Polyester, TP | Mar-Bal |
| TECHNO AES W245 | Techno Polymer Co, Ltd. | AES | TECHNO AES |
| Kumho SSBR SOL-5270H | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Plenco 04504 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |
| Sylvin 916VO-85 Grey 9565 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |