Iupiace® GN10
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Nk8nou_Iupiace-GN10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupiace® GN10 is a Polyphenylene Ether + PS (PPE+PS) material filled with 10% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupiace® GN10: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 83.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 4.5E-5 | cm/cm/°C | |
| Transverse | 7.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 270 to 310 | °C | |
| Mold Temperature | 90.0 to 125 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1695 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SILVER® PA640G30N | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 66 | SILVER® |
| Supol HT143E | LyondellBasell Industries | PP Copolymer | Supol |
| Adell Polyamide BA-36 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Durethan® DP 2131/20 H2.0 900051 | LANXESS GmbH | Nylon 6 | Durethan® |